Some advice from LandGlass about what to do if during the tempering process the fragmentation pieces of tempered glass are too large.
During the quenching process, low quenching pressure will cause large fragmentation pieces of tempered glass. To tackle the issue, it’s possible to increase the quenching pressure settings in tempering parameters. It’s also possible to appropriately reduce the height of the tempering chiller to increase the quenching pressure.
If the glass is not adequately-heated in the heating section, it will also lead to large fragmentation pieces of tempered glass. It’s possible to modify the tempering parameters by either increasing the furnace temperature or extending the heating time of the glass in the heating section, making sure the glass is adequately heated to meet the fragmentation requirements for tempered glass.
24.05.2022, LandGlass
Should the content or the design of these sites violate third parties rights or legal prescriptions, we kindly ask you to send us a respective message without invoice or cost. We guarantee that passages where the claim is considered as justified will be removed immediately, without any necessity to involve any lawyer into this issue. We will reject any claim caused by submission of a honorary note in this regard without any prior contact and confirmation of the issueby us and we reserve the right ssue counter claim ourselves because of violation of aforesaid conditions.